Laminated iron core and manufacturing method of laminated iron core

ABSTRACT

A laminated iron core includes a plurality of blanked iron core pieces laminated together, a continuity of side parts of the iron core pieces configuring a side surface of the laminated iron core. The side part of each iron core piece includes a specific light reflection area having a prescribed width along a circumferential direction, where the specific light reflection area has different light reflection characteristics from the other area of the side part of the iron core piece, and a striped pattern, configured by the specific light reflection areas, exists on the side surface of the laminated iron core.

CROSS REFERENCE TO RELATED APPLICATION(S)

This is a divisional application based on U.S. patent application Ser.No. 15/075,263, filed Mar. 21, 2016, which claims the benefit ofpriority of Japanese Patent Application No. 2015-66468, filed on Mar.27, 2015, the contents of each are incorporated herein by reference inits entirety.

BACKGROUND OF THE INVENTION 1. Field of the Invention

The present invention relates to a laminated iron core and amanufacturing method of a laminated iron core. In particular, thepresent invention relates to a laminated iron core and a manufacturingmethod of a laminated iron core in which when the laminated iron core ismanufactured by using multiple iron core pieces taken from a steelplate, sources of the iron core pieces are easily recognized, when theiron core pieces are turned and laminated to manufacture the laminatediron core, a turned and laminated state of the iron core pieces iseasily recognized, or when the iron core pieces are skewed tomanufacture the laminated iron core, the skew is easily recognized.

2. Description of the Related Art

The laminated iron core forming an electric motor or a generator ismanufactured in such a way that iron core pieces blanked or stamped outfrom a steel plate are laminated. At that time, in order to improve aproductivity or a yield, a blanking die unit layout may be sometimesused that a plurality of iron core pieces are blanked out and formedfrom one steel plate at the same time (namely, the multiple iron corepieces are taken). When the multiple iron core pieces are taken from thesteel plate, which row where the iron core piece forming the laminatediron core is blanked needs to be identified (Namely, the source of theiron core piece is recognized) in order to recognize the quality of themanufactured laminated iron core. Accordingly, in each row that the ironcore is blanked or stamped out, a part of a configuration of the ironcore piece is changed (for instance, small irregularities or cut-outparts are provided in a part of an outer peripheral part or an innerperipheral part of the iron core piece) to identify which row where theiron core piece is blanked out. For instance, two rows of the iron corepieces are taken from the steel plate, as shown in FIGS. 9A and 9B, inone iron core piece 80 which is blanked out from the one row, onerecessed part 82 is formed in an edge part of one through hole 81 of aplurality of through holes formed for cooling. In an iron core piece 83which is blanked out from the other row, two recessed parts 82 areformed in an edge part of one through hole 84 of a plurality of throughholes. FIGS. 9A and 9B also show a shaft hole 85 and a magnet-inserthole 86.

For the purpose of improving a property of the laminated iron core, inan inner part of a blanking die unit or in an outer part of the blankingdie unit, the blanked iron core pieces may be sometimes turned andlaminated or the iron core pieces may be turned and laminated whileskewing. In this case, the turned and laminated state of the iron corepieces or whether or not the skew is assuredly applied to the iron corepieces to laminate the iron core pieces needs to be recognized. At thattime, when a configuration of the iron core piece is symmetrical inrotation, a recognition work cannot be done by a method of anexamination of an external appearance of the laminated iron core. Forinstance, JP-U-64-9437 as Patent Literature 1 discloses that a quantityof skew detecting remark is provided in one or a plurality of positionsin an outer peripheral part of the iron core piece (namely, a part ofthe configuration of the iron core piece is changed).

Patent Literature 1: JP-U-64-9437

SUMMARY OF THE INVENTION

However, as described above, when a special machining work is to beapplied to a part of the outer peripheral part or the inner peripheralpart of the iron core piece to change the configuration, below-describedproblems arise.

1) Symmetrical property in rotation of the iron core piece collapseswhich causes a weight unbalance to be generated in the formed laminatediron core.

2) When the iron core piece has a configuration in which the specialmachining work is applied only to the outer peripheral part, for aproduct (for instance, a rotor of an induction motor or the like) inwhich the cut-out part is hardly formed in its outer peripheral part,the special machining work cannot be applied thereto.3) Since blanking tools (a blanking punch and a blanking die unit) forthe special machining work are necessary, the number of components ofthe blanking die unit is increased to increase a die manufacturing cost.4) A machining method (a manufacturing method) of the blanking toolswhich carry out the special machining work is limited. For instance,when an outer configuration of the blanking tools is a true circle, acylindrical grinding work or a wire electric discharge machining workmay be applied thereto. However, when a cut-out part is partly providedin the outer peripheral part of the blanking tools, the machining methodis limited to the wire electric discharge machining work.

The present invention is devised by considering the above-describedcircumstances, and it is a non-limited object of the present inventionto provide a laminated iron core and a method of a laminated iron corein which rows can be easily recognized where multiple iron core piecestaken from a steel plate are blanked or stamped or a turned andlaminated state or skew of the iron core pieces can be easilyrecognized.

A first aspect of the present invention provides a laminated iron coreincluding: a plurality of blanked iron core pieces laminated together, acontinuity of side parts of the iron core pieces configuring a sidesurface of the laminated iron core, wherein the side part of each ironcore piece includes a specific light reflection area having a prescribedwidth along a circumferential direction, where the specific lightreflection area has different light reflection characteristics from theother area of the side part of the iron core piece, and a stripedpattern, configured by the specific light reflection areas, exists onthe side surface of the laminated iron core.

When the iron core pieces are laminated while being blanked, the stripedpattern is configured by the specific reflection areas being consecutivein a direction of lamination. When the iron core pieces are turned andlaminated for each piece, the striped pattern is configured by thespecific light reflection areas arranged at intervals of prescribedangles along the circumferential direction. When the iron core piecesare turned and laminated for each set of pieces, the striped pattern isconfigured by the specific light reflection areas being consecutivealong a direction of lamination for each set, and arranged at intervalsof prescribed angles along the circumferential direction on the setbasis.

When the iron core pieces are laminated while being skewed, the stripedpattern is configured by the specific light reflection areas beingconsecutive along a direction of lamination with their angular positionsin the circumferential direction gradually changed.

A second aspect of the present invention provides a manufacturing methodof a laminated iron core manufactured by laminating blanked iron corepieces together, the manufacturing method including: providing a firstblanking tool which determines a product configuration of the iron corepieces and a second blanking tool paired with the first blanking tool,wherein a clearance formed between the first and second blanking toolsis partly enlarged by providing a recessed part in a part of a surfaceof the second blanking tool; and blanking a steel plate by the first andsecond blanking tools with the clearance to partly change a ratio offormation of a shearing surface layer to a broken surface layer whichare formed in a form of layers along a blanking direction in a side partof each iron core piece, to thereby form a specific light reflectionarea having a prescribed width and different light reflectioncharacteristics from the other area of the side part of the iron corepiece.

In the laminated iron core according to the first aspect of the presentinvention and the manufacturing method of the laminated iron coreaccording to the second aspect of the present invention, when themultiple iron core pieces are taken from one steel plate to manufacturethe laminated iron core, the specific light reflection area is providedonly in the iron core piece blanked from a specific row, or positions,widths or the number of the specific light reflection areas provided inthe multiple iron core pieces taken from the steel plate are changedrespectively for each of the rows. Thus, even when the configuration ofthe iron core piece is not changed as in the usual laminated iron core,from which rows the iron core pieces are blanked out, can be identified,that form the laminated iron core from a presence or absence of astriped pattern, a position of the striped pattern or the number of thestriped patterns.

Further, the specific light reflection areas are supposed to be formed,for instance, in outer side parts of the iron core pieces. When the ironcore pieces are turned by prescribed angles and laminated (turned andlaminated), since the positions (angular positions in a circumferentialdirection and positions in a direction of lamination) of the specificlight reflection areas are changed in accordance with a turning andlaminating operation, the formed striped pattern is also changed. Whenthe angular positions of the striped patterns adjacent in thecircumferential direction are examined, the turned and laminated stateof the iron core pieces can be easily recognized. When the iron corepieces are skewed and laminated, the striped pattern is formed in whichthe specific light reflection areas are continuous in the outer sidesurface of the laminated iron core with their angular positions in thecircumferential direction gradually changed. Thus, when an angle ofinclination of the striped pattern is observed, the skew can be easilyrecognized.

BRIEF DESCRIPTION OF THE DRAWINGS

In the accompanying drawings:

FIGS. 1A and 1B respectively show perspective views of laminated ironcores of a first exemplary embodiment and a second exemplary embodimentof the present invention;

FIG. 2A is a plan view showing a relation between a blanking punch and ablanking die unit used to blank an outer shape of an iron core pieceused for manufacturing the laminated iron core;

FIG. 2B is an enlarged view of a part P in FIG. 2A;

FIG. 3A is a schematic view showing a state when a steel plate isblanked by the blanking die unit and a non-recessed part of the blankingpunch;

FIG. 3B is a schematic view showing a state that the steel plate isblanked by the blanking die unit and a recessed part of the blankingpunch;

FIG. 4A is a schematic view showing a state of a side part of the ironcore piece which is blanked by the non-recessed part of the blankingpunch;

FIG. 4B is a schematic view showing a state of the side part of the ironcore piece which is blanked by the recessed part of the blanking punch;

FIGS. 5A and 5B respectively show partly cut-out perspective views oflaminated iron cores according to third and fourth exemplary embodimentsof the present invention;

FIG. 6A is a plan view showing a relation between a blanking punch and ablanking die unit used to blank an inner shape of an iron core pieceused for manufacturing the laminated iron core;

FIG. 6B is an enlarged view of a part Q in FIG. 6A;

FIG. 7A is a schematic view showing a state when a steel plate isblanked by a non-recessed part of the blanking die unit and the blankingpunch.

FIG. 7B is a schematic view showing a state that the steel plate isblanked by a recessed part of the blanking die unit and the blankingpunch;

FIG. 8A is a schematic view showing a state when the inner shape isblanked in the steel plate by the non-recessed part of the blanking dieunit and the blanking punch;

FIG. 8B is a schematic view showing a state when the inner shape isblanked in the steel plate by the recessed part of the blanking die unitand the blanking punch; and

FIGS. 9A and 9B are plan views of an iron core piece according to ausual example.

DETAILED DESCRIPTION OF THE EXEMPLARY EMBODIMENTS

Subsequently, by referring to the accompanying drawings, exemplaryembodiments which embody the present invention will be described tounderstand the present invention.

A laminated iron core 10 according to a first exemplary embodiment ofthe present invention shown in FIG. 1A is manufactured by carrying out alamination (a turning and laminating operation) that every time aplurality (N sheets) of iron core pieces 11 circular in plan view arelaminated, the iron core pieces are turned by 180°. Here, specific lightreflection areas 12 having different light reflection characteristicsfrom other areas and prescribed widths, for instance, widths of 0.5 to1.5 mm are provided along a circumferential direction in side parts ofthe iron core pieces 11. As a result, on a side surface 13 (formed insuch a way that the side parts of the iron core pieces 11 are continuedin a direction of lamination) of the laminated iron core 10 formed bylaminating the iron core pieces 11, striped patterns 14 areintermittently provided that are formed in such a way that N pieces ofspecific light reflection areas 12 are continuously arranged in thedirection of lamination at intervals of 180° along the circumferentialdirection.

FIG. 1A shows a shaft hole 15 of the laminated iron core 10, amagnet-insert hole 16, and a cooling hole 17 formed in the laminatediron core 10.

A laminated iron core 18 according to a second exemplary embodiment ofthe present invention shown in FIG. 1B is manufactured in such a waythat iron core pieces 11 are skewed and laminated at the same time. As aresult, on a side surface 19 of the laminated iron core 18 formed by thecontinuity of side parts of the iron core pieces 11, a striped pattern20 is provided which is formed in such a manner that specific lightreflection areas 12 are continuously arranged in a direction oflamination by gradually changing their angular positions in acircumferential direction (the specific light reflection areas areshifted at angles of rotation applied when skewing).

In a manufacturing method of the laminated iron cores 11 and 18according to the first and second exemplary embodiments, for a blankingdie unit 22 (one example of a first blanking tool) and a blanking punch23 (one example of a second blanking tool) paired with the blanking dieunit 22 which are used to blank and form the iron core pieces 11 from asteel plate 21 (see FIGS. 3A and 3B), as shown in FIG. 2A, an insidediameter dimension D₁ of the blanking die unit 22 which determines anouter shape (one example of a product configuration) of the iron corepiece 11 is allowed to match with an outside diameter dimension of theiron core piece 11. As shown in FIG. 2B, a recessed part 24 is providedin a part of a surface (an outer peripheral part) of the blanking punch23. Thus, a clearance C which is formed between a bottom surface of therecessed part 24 on the surface of the blanking punch 23 and an innerperipheral surface of the blanking die unit 22 is enlarged more than aclearance C₀ formed between a non-recessed part of the surface (theouter peripheral part) of the blanking punch 23 and the inner peripheralsurface of the blanking die unit 22. Here, a width W of the recessedpart 24 is set to, for instance, 0.5 to 1.5 mm. Further, when athickness of the steel plate 21 is supposed to be set to t, theclearance C₀ is set to, for instance, 0.05 t to 0.2 t. A depth D of therecessed part 24 is set to, for instance, 0.05 t to 0.5 t. Accordingly,the clearance C is set to 0.1 t to 0.7 t.

In a case where the outer shape of the iron core piece 11 is blanked outfrom the steel plate 21 by using the blanking die unit 22 and theblanking punch 23, when the blanking punch 23 is lowered, the blankingpunch 23 comes into contact with the steel plate 21. A cutting edge ofthe blanking punch 23 and a cutting edge of the blanking die unit 22respectively bite the steel plate 21. At this time, as shown in FIG. 3A,in an area of the clearance C₀ (between the non-recessed part of thesurface of the blanking punch 23 and the inner peripheral surface of theblanking die unit 22), sags 25 and 26 are formed respectively in a frontsurface side of the steel plate 21 (the blanking punch 23 side) and aback surface side (the blanking die unit 22 side) of the steel plate 21.As shown in FIG. 3B, in an area of the clearance C (between the recessedpart 24 on the surface of the blanking punch 23 and the inner peripheralsurface of the blanking die unit 22), sags 25 a and 26 a are formedrespectively in the front surface side (the blanking punch 23 side) andthe back surface side (the blanking die unit 22 side) of the steel plate21. Widths of the sags 25 a and 26 a generated in the area of theclearance C are larger than widths of the sags 25 and 26 generated inthe area of the clearance C₀.

Further, when the blanking punch 23 is lowered, a steel plate materialin the vicinity of the cutting edge of the blanking die unit 22 and thecutting edge of the blanking punch 23 collapses. The cutting edge of theblanking die unit 22 and the cutting edge of the blanking punch 23respectively generate a shearing deformation in the steel plate materialand deeply bite the steel plate material. As a result, as shown in FIG.3A, in the area of the clearance C₀, the steel plate material comes intocontact with the inner peripheral surface of the blanking die unit 22 toform a shearing surface 27, and comes into contact with the outerperipheral surface of the blanking punch 23 to form a shearing surface28, respectively. As shown in FIG. 3B, in the area of the clearance C,the steel plate material comes into contact with the inner peripheralsurface of the blanking die unit 22 to form a shearing surface 27 a, andcomes into contact with the bottom surface of the recessed part 24 ofthe blanking punch 23 to form a shearing surface 28 a, respectively.

When the blanking punch 23 is lowered more so that the cutting edge ofthe blanking die unit 22 and the cutting edge of the blanking punch 23respectively bite more deeply the steel plate material, a work hardeningis generated in the steel plate material to increase a shearing force.Thus, cracks are generated respectively in the vicinity of the cuttingedges of the blanking die unit 22 and the blanking punch 23. As shown inFIGS. 3A and 3B, the cracks grow to be combined together, so that brokensurfaces 29 and 29 a are formed to blank out the outer shape of the ironcore piece 11 from the steel plate 21. Here, in the side part of theiron core piece 11, the shearing surfaces 27 and 27 a are most protrudeoutward in a radial direction. Since the shearing surfaces 27 and 27 aare formed in such a way that the cutting edge of the blanking die unit22 is allowed to bite the steel plate material, the shearing surfaces 27and 27 a exist on the same circumference. Even when the recessed part 24is provided in a part of the surface of the blanking punch 23, theconfiguration of the iron core piece 11 is not changed.

Here, as shown in FIGS. 4A and 4B, the width of the sag 26 a generatedin the area of the clearance C is larger than the width of the sag 26generated in the area of the clearance C₀ (the same as a relationbetween the sags 25 and 25 a). Thus, in the area of the clearance C, thework hardening is generated more early than that in the area of theclearance C₀. Accordingly, a width of the shearing surface 27 a (a widthalong a lowering direction of the blanking punch 23) is smaller than awidth of the shearing surface 27 (the same as a relation between theshearing surfaces 28 and 28 a). As a result, a width of the brokensurface 29 a is larger than a width of the broken surface 29. Burrs 30and 30 a are generated when the iron core piece 11 is blanked out.

As shown in FIGS. 4A and 4B, in the side part of the iron core piece 11,in an area formed correspondingly to the area of the clearance C₀, alayer of the shearing surface 27 and a layer of the broken surface 29exist which are formed in configurations of layers along a blankingdirection of the blanking punch 23. In an area formed correspondingly tothe area of the clearance C, a layer of the shearing surface 27 a and alayer of the broken surface 29 a exist which are formed inconfigurations of layers along the blanking direction of the blankingpunch 23. Here, the layer of the shearing surface 27 is larger than thelayer of the shearing surface 27 a in its width. The layer of the brokensurface 29 is smaller than the layer of the broken surface 29 a in itswidth. Accordingly, a ratio of formation of the layer of the brokensurface 29 a to the layer of the shearing surface 27 a in the areaformed correspondingly to the area of the clearance C is larger than aratio of formation of the layer of the broken surface 29 to the layer ofthe shearing surface 27 in the area formed correspondingly to the areaof the clearance C₀.

Since the shearing surfaces 27 and 27 a are flat surfaces, lightsincident on the shearing surfaces 27 and 27 a are reflected towardspecific directions determined by directions on which the lights areincident. However, since many microscopic surfaces which are directed tovarious directions exist in the broken surfaces 29 and 29 a, lightsincident on the broken surfaces 29 and 29 a are irregularly reflected.

Accordingly, in the side part of the iron core piece 11, when the lightsare respectively incident on an area with a prescribed width having theshearing surface 27 a and the broken surface 29 a along thecircumferential direction and a remaining area having the shearingsurface 27 and the broken surface 29, a ratio of existence of the brokensurface in the area with the prescribed width is higher than that in theremaining area, so that a difference arises in a state of irregularreflection of the lights (one example of the light reflectioncharacteristics). Accordingly, in the side part of the iron core piece11, the area with the prescribed width having the shearing surface 27 aand the broken surface 29 a serves as the specific light reflection area12.

When the iron core pieces 11 are laminated to manufacture the laminatediron cores 10 and 18, on the side surfaces 13 and 19 of the laminatediron cores 10 and 18, the specific light reflection areas 12 arecontinuously arranged in the direction of lamination. Accordingly, thelights are allowed to be incident on the side surfaces 13 and 19 of thelaminated iron cores 10 and 18 and the side surfaces 13 and 19 of thelaminated iron cores 10 and 18 are observed from directions deviatingfrom light reflection directions by the shearing surfaces 27 and 27 a.Thus, since the state of the light irregular reflection is distinguishedin a range where the specific light reflection areas 12 are continuouslyarranged along the direction of lamination, one bright striped pattern14 and 20 are recognized which have substantially the same width as thatof the specific light reflection area 12.

Thus, in the laminated iron core 10, when the angular positions of thestriped patterns 14 in the circumferential direction which exist in theside surface 13 of the laminated iron core 10 are examined, the turnedand laminated states of the iron core pieces 11 can be easilyrecognized. In the laminated iron core 18, when the angle of inclinationof the striped pattern 20 in the direction of lamination which exists inthe side surface 19 of the laminated iron core 18 is examined, the skewapplied to the iron core pieces 11 can be easily recognized. In order toform the specific light reflection areas 12, the recessed part 24 may bemerely provided in a part of the surface of the blanking punch 23 as theblanking tool B. Thus, the blanking punch 23 can be easily machined.

Further, in the side surfaces 13 and 19 of the laminated iron cores 10and 18, a part in which the striped patterns 14 and 20 are generated ismerely different from a part in which the striped patterns 14 and 20 arenot generated in a ratio of a total area of the shearing surfaces to atotal area of the broken surfaces which appear in the side surfaces 13and 19. A configuration (dimension) does not change. Accordingly, achange of design due to the change of the configuration does not arise.A deterioration of the quality of a product (for instance, a weightunbalance which is caused by a collapse of a symmetrical property inrotation) does not occur.

A laminated iron core 31 according to a third exemplary embodiment ofthe present invention shown in FIG. 5A is manufactured by carrying out alamination (a turning and laminating operation) that every time aplurality (N sheets) of iron core pieces 32 are laminated, the iron corepieces 32 are turned by 180°. Here, specific light reflection areas 33having different light reflection characteristics from the other areaand prescribed widths, for instance, widths of 0.5 to 1.5 mm areprovided along a circumferential direction in side parts of throughholes formed in central parts of the iron core pieces 32. As a result,on a side surface 34 of a shaft hole (formed in such a way that the sideparts of the through holes formed in the iron core pieces 32 arecontinued in a direction of lamination) of the laminated iron core 31formed by laminating the iron core pieces 32, striped patterns 35 areintermittently provided that are formed in such a way that N pieces ofspecific light reflection areas 33 are continuously arranged atintervals of 180° in the circumferential direction along the directionof lamination.

A laminated iron core 36 according to a fourth exemplary embodiment ofthe present invention shown in FIG. 5B is manufactured in such a waythat skew is applied to iron core pieces 32 and the iron core pieces 32are laminated at the same time. As a result, on a side surface 37 of ashaft hole of the laminated iron core 36 formed by the continuity ofside parts of through holes formed in central parts of the iron corepieces 32, a striped pattern 39 is provided which is formed in such amanner that specific light reflection areas 33 are continuously arrangedin a direction of lamination by gradually changing their angularpositions in a circumferential direction (the specific light reflectionareas are shifted at angles of rotation applied when skewing).

In a manufacturing method of the laminated iron cores 31 and 36according to the third and fourth exemplary embodiments, for a blankingdie unit 40 (one example of a second blanking tool) and a blanking punch41 (one example of a first blanking tool) paired with the blanking dieunit 40 which are used to blank and form the through holes in thecentral parts of the iron core pieces 32 from a steel plate 21 (seeFIGS. 7A and 7B), as shown in FIG. 6A, an outside diameter dimension D₀of the blanking punch 41 which determines an inner shape (one example ofa product configuration) of the through hole formed in the iron corepiece 32 is allowed to match with an inside diameter dimension of thethrough hole. As shown in FIG. 6B, a recessed part 42 is provided in apart of an inner peripheral surface (an inner peripheral part) of theblanking die unit 40. Thus, a clearance C which is formed between abottom surface of the recessed part 42 provided in the blanking die unit40 and an outer peripheral surface of the blanking punch 41 is enlargedmore than a clearance C₀ formed between a non-recessed part of the innerperipheral surface of the blanking die unit 40 and the outer peripheralsurface (an outer peripheral part) of the blanking punch 41. Here, awidth W of the recessed part 42 is set to, for instance, 0.5 to 1.5 mm.Further, when a thickness of the steel plate 21 is supposed to be set tot, the clearance C₀ is set to, for instance, 0.05 t to 0.2 t. A depth Dof the recessed part 42 is set to, for instance, 0.05 t to 0.5 t.Accordingly, the clearance C is set to 0.1 t to 0.7 t.

When an inner shape of the iron core piece 32 which has the through holeformed in the central part of the iron core piece 32 is blanked out fromthe steel plate 21 by using the blanking die unit 40 and the blankingpunch 41, if the blanking punch 41 is lowered, the blanking punch 41comes into contact with the steel plate 21. A cutting edge of theblanking punch 41 and a cutting edge of the blanking die unit 40respectively bite the steel plate 21. At this time, as shown in FIG. 7A,in an area of the clearance C₀ formed (between the non-recessed part ofthe inner peripheral surface of the blanking die unit 40 and the outerperipheral surface of the blanking punch 41), sags 43 and 44 are formedrespectively in a front surface side of the steel plate 21 (the blankingpunch 41 side) and a back surface side (the blanking die unit 40 side)of the steel plate 21. As shown in FIG. 7B, in an area of the clearanceC formed (between the bottom surface of the recessed part 42 in theinner peripheral surface of the blanking die unit 40 and the outerperipheral surface of the blanking punch 41), sags 43 a and 44 a areformed respectively in the front surface side (the blanking punch 41side) and the back surface side (the blanking die unit 40 side) of thesteel plate 21. Widths of the sags 43 a and 44 a generated in the areaof the clearance C are larger than widths of the sags 43 and 44generated in the area of the clearance C₀.

Further, when the blanking punch 41 is lowered, a steel plate materialin the vicinity of the cutting edge of the blanking die unit 40 and thecutting edge of the blanking punch 41 collapses. The cutting edge of theblanking die unit 40 and the cutting edge of the blanking punch 41respectively generate a shearing deformation in the steel plate materialand deeply bite the steel plate material. As a result, as shown in FIG.7A, in the area of the clearance C₀, the steel plate material comes intocontact with the inner peripheral surface of the blanking die unit 40 toform a shearing surface 45, and comes into contact with the outerperipheral surface of the blanking punch 41 to form a shearing surface46, respectively. As shown in FIG. 7B, in the area of the clearance C,the steel plate material comes into contact with the bottom surface ofthe recessed part 42 of the blanking die unit 40 to form a shearingsurface 45 a, and comes into contact with the outer peripheral surfaceof the blanking punch 41 to form a shearing surface 46 a, respectively.

When the blanking punch 41 is lowered more so that the cutting edge ofthe blanking die unit 40 and the cutting edge of the blanking punch 41respectively bite more deeply the steel plate material, a work hardeningis generated in the steel plate material to increase a shearing force.Thus, cracks are generated respectively in the vicinity of the cuttingedges of the blanking die unit 40 and the blanking punch 41. As shown inFIGS. 7A and 7B, the cracks grow to be combined together, so that brokensurfaces 47 and 47 a are formed to blank out the inner shape of the ironcore piece 32 (the through hole is blanked out) from the steel plate 21.Here, in the side part of through hole formed in the iron core piece 32,the shearing surfaces 46 and 46 a most protrude inward in a radialdirection. Since the shearing surfaces 46 and 46 a are formed in such away that the cutting edge of the blanking punch 41 is allowed to bitethe steel plate material, the shearing surfaces 46 and 46 a exist on thesame circumference. Even when the recessed part 42 is provided in a partof the inner peripheral surface of the blanking die unit 40, theconfiguration of the through hole formed in the iron core piece 32 isnot changed.

Here, as shown in FIGS. 8A and 8B, the width of the sag 43 a generatedin the area of the clearance C is larger than the width of the sag 43generated in the area of the clearance C₀ (the same as a relationbetween the sags 44 and 44 a). Thus, in the area of the clearance C, thework hardening is generated more early than that in the area of theclearance C₀. Accordingly, a width of the shearing surface 46 a (a widthalong a lowering direction of the blanking punch 41) is smaller than awidth of the shearing surface 46 (the same as a relation between theshearing surfaces 45 and 45 a). As a result, a width of the brokensurface 47 a is larger than a width of the broken surface 47. Referencenumerals 48 and 48 a designate burrs generated when the through hole isblanked out and formed.

On the side part of the through hole of the iron core piece 32, in anarea formed correspondingly to the area of the clearance C₀, a layer ofthe shearing surface 46 and a layer of the broken surface 47 exist whichare formed in configurations of layers along a blanking direction of theblanking punch 41. In an area formed correspondingly to the area of theclearance C, a layer of the shearing surface 46 a and a layer of thebroken surface 47 a exist which are formed in configurations of layersalong the blanking direction of the blanking punch 41. Here, the layerof the shearing surface 46 is larger than the layer of the shearingsurface 46 a in its width. The layer of the broken surface 47 is smallerthan the layer of the broken surface 47 a in its width. Accordingly, aratio of formation of the layer of the broken surface 47 a to the layerof the shearing surface 46 a in the area formed correspondingly to thearea of the clearance C is larger than a ratio of formation of the layerof the broken surface 47 to the layer of the shearing surface 46 in thearea formed correspondingly to the area of the clearance C₀.

Since the shearing surfaces 46 and 46 a are flat surfaces, lightsincident on the shearing surfaces 46 and 46 a are reflected towardspecific directions determined by directions on which the lights areincident. However, since many microscopic surfaces which are directed tovarious directions exist in the broken surfaces 47 and 47 a, lightsincident on the broken surfaces 47 and 47 a are irregularly reflected.

Accordingly, in the side part of the through hole of the iron core piece32, when the lights are respectively incident on an area with aprescribed width having the shearing surface 46 a and the broken surface47 a along the circumferential direction and a remaining area having theshearing surface 46 and the broken surface 47, a ratio of existence ofthe broken surface in the area with the prescribed width is higher thanthat in the remaining area, so that a difference arises in a state ofirregular reflection of the lights (one example of the light reflectioncharacteristics). Accordingly, in the side part of the through hole ofthe iron core piece 32, the area with the prescribed width having theshearing surface 46 a and the broken surface 47 a serves as the specificlight reflection area 33.

When the iron core pieces 32 are laminated to manufacture the laminatediron cores 31 and 36, on the side surfaces 34 and 37 of the shaft holesof the laminated iron cores 31 and 36, the specific light reflectionareas 33 are continuously arranged in the direction of lamination.Accordingly, the lights are allowed to be incident on the side surfaces34 and 37 of the shaft holes of the laminated iron cores 31 and 36 andthe side surfaces 34 and 37 of the shaft holes of the laminated ironcores 31 and 36 are observed from directions deviating from lightreflection directions by the shearing surfaces 46 and 46 a. Thus, sincethe state of the light irregular reflection is distinguished in a rangewhere the specific light reflection areas 33 are continuously arrangedalong the direction of lamination, bright striped patterns 35 and 39 arerecognized which have substantially the same width as that of thespecific light reflection area 33.

Thus, in the laminated iron core 31, when the angular positions of thestriped patterns 35 in the circumferential direction which exist in theside surface 34 of the shaft hole of the laminated iron core 31 areexamined, the turned and laminated states of the iron core pieces 32 canbe easily recognized. In the laminated iron core 36, when the angle ofinclination of the striped pattern 39 in the direction of laminationwhich exists in the side surface 37 of the shaft hole of the laminatediron core 36 is examined, the skew applied to the iron core pieces 32can be easily recognized. In order to form the specific light reflectionareas 33, the recessed part 42 may be merely provided in a part of theinner peripheral surface of the blanking die unit 40 as the blankingtool B. Thus, the blanking die unit 40 can be easily machined.

Further, in the side surfaces 34 and 37 of the shaft holes of thelaminated iron cores 31 and 36, a part in which the striped patterns 35and 39 are generated is merely different from a part in which thestriped patterns 35 and 39 are not generated in a ratio of a total areaof the shearing surfaces to a total area of the broken surfaces whichappear in the side surfaces 34 and 37. A configuration (dimension) doesnot change. Accordingly, a change of design does not arise due to thechange of the configuration. A deterioration of the quality of a product(for instance, a weight unbalance which is caused by a collapse of asymmetrical property in rotation) does not occur.

Here, the specific light reflection areas 33 are provided in the sideparts of the through holes forming the shaft holes, however, thespecific light reflection areas may be provided in side parts of otherthrough holes which form a magnet-insert hole 16 or a cooling hole 17.

The present invention is described above by referring to the exemplaryembodiments. However, the present invention is not limited to thestructures described in the exemplary embodiment and may include otherexemplary embodiments or modified examples which may be consideredwithin a range of matters described in claims.

Further, combinations of component elements included respectively in thepresent exemplary embodiments, other exemplary embodiments or themodified examples may be incorporated in the present invention.

Further, in the above-described exemplary embodiment, the specific lightreflection areas are formed in the outer side part of the iron corepiece or the inner peripheral part of the through hole of the iron corepiece to recognize the turned or laminated state of the iron core piecesor the skew. However, for instance, when two rows of iron core piecesare taken from one steel plate to manufacture the laminated iron core,the specific light reflection area may be provided in the iron corepiece blanked from a specific row. When three rows or more, or multiplerows of iron core pieces are taken to manufacture the laminated ironcore, positions, widths or the number of the specific light reflectionareas to be formed can be changed for each of rows (in this case, astriped pattern is formed in such a way that the specific lightreflection areas are continuously arranged in a direction oflamination). Thus, which row where the iron core piece forming thelaminated iron core is blanked can be identified from the presence orabsence of the striped pattern, the position of the striped pattern, thewidth of the striped pattern or the number of the striped patternswithout changing a configuration of the iron core piece for each of therows. Thus, the laminated iron core having an excellent property can beeasily manufactured.

Further, in an example explained in the above-described exemplaryembodiments, the turning and laminating operation is carried out thatevery time a plurality of iron core pieces are laminated, the iron corepieces are turned by 180°. However, a turning and laminating operationmay be carried out that every time a plurality of iron core pieces arelaminated, the iron core pieces are turned by a prescribed angle otherthan 180° (a striped pattern is formed in such a way that a plurality ofspecific light reflection areas are continuously arranged at intervalsof prescribed angles in a circumferential direction along a direction oflamination). Otherwise, a turning and laminating operation may becarried out that every time one iron core piece is laminated, the ironcore piece is turned by a prescribed angle (a striped pattern is formedin such a way that the specific light reflection areas are arranged atintervals of prescribed angles along a circumferential direction).

The clearances of the blanking die unit and the blanking punch aresuitably set depending on the blanked configuration or the quality ofthe iron core piece or manufacturing conditions (a blanking speed, asimultaneous blanking of a plurality of iron core pieces or the like).Depth of the recessed part is set so as to meet the above-describedconditions.

What is claimed is:
 1. A laminated iron core comprising: a plurality of blanked iron core pieces laminated together, a continuity of side parts of the iron core pieces configuring a side surface of the laminated iron core, wherein the side part of each iron core piece includes a specific light reflection area having a prescribed width along a circumferential direction, where the specific light reflection area has different light reflection characteristics from the other area of the side part of the iron core piece, a striped pattern, configured by the specific light reflection areas, exists on the side surface of the laminated iron core, a sag that is generated in the specific light reflection area is adjacent to a shearing surface, and a width of the sag that is generated in the specific light reflection area is different from a width of a sag that is generated in the other area.
 2. The laminated iron core according to claim 1, wherein the striped pattern is configured by the specific light reflection areas arranged at intervals of prescribed angles along the circumferential direction.
 3. The laminated iron core according to claim 1, wherein the striped pattern is configured by the specific light reflection areas being consecutive along a direction of lamination for each set, and arranged at intervals of prescribed angles along the circumferential direction on the set basis.
 4. The laminated iron core according to claim 1, wherein the striped pattern is configured by the specific light reflection areas being consecutive along a direction of lamination with their angular positions in the circumferential direction gradually changed.
 5. The laminated iron core according to claim 1, wherein the striped pattern is configured by the specific reflection areas being consecutive in a direction of lamination.
 6. The laminated iron core according to claim 1, wherein the specific light reflection area at least includes a broken surface, the shearing surface, and the sag.
 7. The laminated iron core according to claim 6, wherein the broken surface and the shearing surface are formed in laminae. 